| Temperature distribution and conduction characteristics of metal oxide varistor in the thermal stability experiments |
| XIAO Xing1, WANG Jianzhong2 |
1. Beijing Leishan Testing Service Center of Lightning Protection Facilities, Beijing 102200;
2. Aerospace Leishan (Beijing) Institute of Metrology Technology, Beijing 102200 |
|
|
|
|
Abstract With the increasing performance requirements of electronic devices, metal oxide varistor (MOV) chips, as important electrical protection components, are widely used in areas such as surge protection. The temperature distribution and conduction characteristics of MOV during operation affect its performance and reliability. This paper experimentally studies the temperature distribution of MOV chips in thermal stability tests and analyzes the impact of temperature non-uniformity on chip performance. The research results show that during the experiment, the highest temperatures of chips with and without a shell are similar and located in the central area. After stabilization, the highest temperature of the shell is 56.5℃ lower than that of the chip on average, and the temperature difference ratio between the inside and outside of the shell remains at around 38% at various current levels. Temperature non- uniformity may lead to local overheating, thereby accelerating chip aging and failure. The research results confirm that the high temperature of MOV often occurs at the electrode pad holes, providing a design basis for its thermal stability test performance and overall thermal separation structure in practical use.
|
|
Received: 31 July 2025
|
|
|
|
| Cite this article: |
|
XIAO Xing,WANG Jianzhong. Temperature distribution and conduction characteristics of metal oxide varistor in the thermal stability experiments[J]. Electrical Engineering, 2026, 27(3): 48-51.
|
|
|
|
| URL: |
|
https://dqjs.cesmedia.cn/EN/Y2026/V27/I3/48
|
[1] 刘冰桦, 周歧斌. 电涌保护器热稳定性试验的研究与分析[J]. 现代建筑电气, 2015, 6(2): 1-4.
[2] 畅雷. 限压型电涌保护器模块散热特性研究[D]. 南京: 南京信息工程大学, 2019.
[3] 李强. 氧化锌压敏电阻热特性研究与分析[D]. 南京: 南京信息工程大学, 2014.
[4] 程卓林, 武康宁, 王佳乐, 等. 稳定型氧化锌压敏电阻高温直流老化的转变特性[J]. 电工技术学报, 2025, 40(9): 2958-2969.
[5] 杨岱礼, 赵洪峰, 王锋, 等. SnO2压敏电阻交流老化机理的探索[J]. 电瓷避雷器, 2024(6): 92-98.
[6] 高婷婷. 氧化锌避雷器局部老化对热电特性影响研究[D]. 沈阳: 沈阳工业大学, 2022.
[7] 张欣, 杨天琦, 杨仲江. 基于瞬态热阻抗的不同电流对MOV芯片散热能力的影响[J]. 电瓷避雷器, 2014(5): 46-48, 54.
[8] 畅雷, 杨仲江, 申东玄. 电阻片与外壳间距对SPD模块散热的影响研究[J]. 电瓷避雷器, 2019(2): 41-46.
[9] 张欣. 基于多种老化模型的氧化锌压敏电阻损坏模式研究[D]. 南京: 南京信息工程大学, 2015.
[10] 黄海博, 孙伟, 万翔, 等. ZnO压敏电阻直流老化特性的研究[J]. 电瓷避雷器, 2021(4): 22-29. |
|
|
|
2026, Vol. 27 